Composition
PROPERTIES OF HANEX®
| Properties | Unit | Result | Test METHOD | REMARK |
|---|---|---|---|---|
| Specific Gravity | g/cm3 | 1.8 | ||
| Tensile Strength | Psi | 5,400 | ASTM D 638 | INSTRON |
| Tensile Modulus | Psi | 1.4x106 | ASTM D 638 | INSTRON |
| Elongation | % min | 0.42 | ASTM D 638 | INSTRON |
| Flexural Strength | Psi | 9,200 | ASTM D 790 | INSTRON |
| Flexural Modulus | Psi | 1.38x105 | ASTM D 790 | INSTRON |
| Hardness (Rockwell) | 92 | ASTM D 785 | M scale | |
| Thermal Expansion | Mm/m c | 3.04x10-5 | ASTM D 696 | |
| Gloss (60° Gardner) | 5 - 20 | ANSI Z124 | ||
| Color Stability | No Change | NEMA LD3 | 200 hours | |
| Wear & Cleanability | Passes | ANSI Z124 | ||
| Boiling Water Surface Resistance | No Change | NEMA LD3 | ||
| High Temperature Resistance | No Change | NEMA LD3 | ||
| Stain Resistance | Passes | NEMA LD3 | ||
| Impact Resistance | No Fracture | NEMA LD3 | 1/4"slab-36"drop-1/2lb ball | |
| IZOD Impact Strength | Ft.1bs/in | 0.28 | ASTM D 256 | Notched |
| Water Absorption Weight | % max | 0.03 | ASTM D 570 | |
| Fungi & Bacteria | No Attack | ANSI Z124 | ||
| Wetherability | No Charge | ASTM D 1499 | 1000 hours |
Chemical Composition
HANEX®
| Material Name | Remark |
|---|---|
| MMA (Methyl Methacrylate) | Resin |
| PMMA (Polymethyl Methacrylate) | Resin |
| AL (OH)3 - Alumina Trihydrate | Filler |
| UV Absorbers, Cross Linking Agents, Stabilisers, Curing Agents, Etc. | Additives |
Early Fire Hazard Indices
| Indices | Results | Range |
|---|---|---|
| Ignitability | 9 | 0 - 20 |
| Spread Of Flame Index | 0 | 0 - 10 |
| Heat Evolved Index | 1 | 0 - 10 |
| Smoke Density Index | 0 | 0 - 10 |
** Indices when tested to ASTM E-84-01 in SGS U.S. Testing Company Inc. 2-2003
** Note: Test results may vary due to color and particulate size. However, result changes will only be minor.
CHEMICAL STAIN AND RESISTANCE
HANEX® is an acrylic solid surface with a high level of alumina trihydrate content as the filler, an ingredient which provides superior resistance to stains and chemicals. However exposure to harsh chemicals should be avoided. In case of surface contamination, quickly flush affected area with a domestic gritty cleaner and water. Sand if necessary, as a rule of thumb, surface damage may vary with the chemical strength and exposed time.